The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k

Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. Wit...

Full description

Bibliographic Details
Main Authors:	Ani, Mohd Hanafi, Othman, Raihan
Format:	Monograph
Language:	English
Published:	s.n. 2012
Subjects:	TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering
Online Access:	http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/1/EDW-B0906-333..pdf

id	iium-32502
recordtype	eprints
spelling	iium-325022015-05-18T02:01:25Z http://irep.iium.edu.my/32502/ The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k Ani, Mohd Hanafi Othman, Raihan TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. With the presence of water vapor in humid environment the formation of void will increase, thus greater number of void compared to that in dry environment s.n. 2012-01-04 Monograph NonPeerReviewed application/pdf en http://irep.iium.edu.my/32502/1/EDW-B0906-333..pdf Ani, Mohd Hanafi and Othman, Raihan (2012) The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k. Research Report. s.n., Kuala Lumpur. (Unpublished) EDW B0906-333
repository_type	Digital Repository
institution_category	Local University
institution	International Islamic University Malaysia
building	IIUM Repository
collection	Online Access
language	English
topic	TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering
spellingShingle	TA Engineering (General). Civil engineering (General) TK Electrical engineering. Electronics Nuclear engineering Ani, Mohd Hanafi Othman, Raihan The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
description	Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. With the presence of water vapor in humid environment the formation of void will increase, thus greater number of void compared to that in dry environment
format	Monograph
author	Ani, Mohd Hanafi Othman, Raihan
author_facet	Ani, Mohd Hanafi Othman, Raihan
author_sort	Ani, Mohd Hanafi
title	The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
title_short	The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
title_full	The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
title_fullStr	The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
title_full_unstemmed	The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k
title_sort	effects of water vapor on high temperature oxidation of fe-cr-ni alloy at 1073k
publisher	s.n.
publishDate	2012
url	http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/ http://irep.iium.edu.my/32502/1/EDW-B0906-333..pdf
first_indexed	2023-09-18T20:46:54Z
last_indexed	2023-09-18T20:46:54Z
_version_	1777409735626063872

The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k

Similar Items