Physical properties of electroless nickel-tungsten coating on mild steels obtained from acetic bath
Electroless deposition of nickel tungsten on mild steel was conducted using acetic bath, containing nickel sulphate and sodium tungstate in the alkaline medium. The influence of sodium acetate and sodium tungstate on deposits was investigated and characterized using scanning electron microscope (...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Trans Tech Publications Ltd., Switzerland
2015
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/48506/ http://irep.iium.edu.my/48506/ http://irep.iium.edu.my/48506/ http://irep.iium.edu.my/48506/1/48506_-_Physical_properties_of_electroless_nickel-tungsten_coating_on_mild_steels_obtained_from_acetic_bath.pdf |
| Summary: | Electroless deposition of nickel tungsten on mild steel was conducted using acetic bath, containing
nickel sulphate and sodium tungstate in the alkaline medium. The influence of sodium acetate and
sodium tungstate on deposits was investigated and characterized using scanning electron
microscope (SEM), energy dispersive X-ray spectrometer (EDX) and x-ray diffraction (XRD) to
assess the phase, content and microstructure features. The surface roughness of coating was
measured using atomic force microscope (AFM) while the hardness was investigated using Vickers
microhardness. The results show that deposits have smooth surfaces, Ra = 0.53 µm, with a
nanocrystalline structure, crystallite size hardness of deposits decreases as the concentration of
sodium tungstate increases.
|
|---|