Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal

This study involved the fabrication of lithium ion solid electrolyte in the Li2O-TiO2-P2O5 (LTP) system. All samples were prepared using mechanical milling (MM)method. The precursor TiO2-P2O5 (TP) system were first fabricated and characterized by Electrochemical Impedance Spectroscopy (EIS), X-Ray D...

Full description

Bibliographic Details
Main Author:	Ahmad Faizal, Ahmad Fuzairi
Format:	Thesis
Language:	English
Published:	2014
Subjects:	Electricity and magnetism Electrolytes, electrolyte solutions
Online Access:	http://ir.uitm.edu.my/id/eprint/13820/ http://ir.uitm.edu.my/id/eprint/13820/1/TM_AHMAD%20FUZAIRI%20AHMAD%20FAIZAL%20AS%2014_5%201.pdf

id	uitm-13820
recordtype	eprints
spelling	uitm-138202016-05-14T07:27:00Z http://ir.uitm.edu.my/id/eprint/13820/ Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal Ahmad Faizal, Ahmad Fuzairi Electricity and magnetism Electrolytes, electrolyte solutions This study involved the fabrication of lithium ion solid electrolyte in the Li2O-TiO2-P2O5 (LTP) system. All samples were prepared using mechanical milling (MM)method. The precursor TiO2-P2O5 (TP) system were first fabricated and characterized by Electrochemical Impedance Spectroscopy (EIS), X-Ray Diffractometer (XRD), Field Emission Scanning Electrone Microscope (FESEM) and laser particle sizer. The highest room temperature conductivity was obtained for 60 wt.% of TiO2-40 wt.% of P2O5 (TP 40) and TP 40 sintered at 900 °C (TP 900) with values of 3.18 x 10-7 Scm-1 and 8.13 X 10-7 Scm-1 respectively. XRD studies showed presence of TiP2O7 peaks in the diffraction pattern of TP 40 as well as TP 900. FESEM micrographs showed agglomeration of the samples as the sintering temperature changed indicating availability of big and small grains. Small grains increased as sintering temperature increased. The size of the particle of the TP samples were estimated to range from 0.70 µm to 3.01 µm for sintered and unsintered samples. In the LTP system, the highest conductivity obtained for the unsintered sample, LTP 15 and sintered LTP 15 (LTP 900) is 6.89 x 10-6 Scm-1 and 3.03 x 10-5 Scm-1 respectively. The diffraction pattern indicate the presence of LiTi2(P04)3 peaks which is the conducting phase.Small grains were observed in all sintered samples with increase in as sintering temperature increases. The sizes of particle of LTP samples were decreased to as low as 200 nm. Temperature dependance studied showed that the conductivity obeys Arrhenius rule indicating that the conductivity is thermally activated. 2014 Thesis NonPeerReviewed text en http://ir.uitm.edu.my/id/eprint/13820/1/TM_AHMAD%20FUZAIRI%20AHMAD%20FAIZAL%20AS%2014_5%201.pdf Ahmad Faizal, Ahmad Fuzairi (2014) Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal. Masters thesis, Universiti Teknologi MARA.
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Teknologi MARA
building	UiTM Institutional Repository
collection	Online Access
language	English
topic	Electricity and magnetism Electrolytes, electrolyte solutions
spellingShingle	Electricity and magnetism Electrolytes, electrolyte solutions Ahmad Faizal, Ahmad Fuzairi Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal
description	This study involved the fabrication of lithium ion solid electrolyte in the Li2O-TiO2-P2O5 (LTP) system. All samples were prepared using mechanical milling (MM)method. The precursor TiO2-P2O5 (TP) system were first fabricated and characterized by Electrochemical Impedance Spectroscopy (EIS), X-Ray Diffractometer (XRD), Field Emission Scanning Electrone Microscope (FESEM) and laser particle sizer. The highest room temperature conductivity was obtained for 60 wt.% of TiO2-40 wt.% of P2O5 (TP 40) and TP 40 sintered at 900 °C (TP 900) with values of 3.18 x 10-7 Scm-1 and 8.13 X 10-7 Scm-1 respectively. XRD studies showed presence of TiP2O7 peaks in the diffraction pattern of TP 40 as well as TP 900. FESEM micrographs showed agglomeration of the samples as the sintering temperature changed indicating availability of big and small grains. Small grains increased as sintering temperature increased. The size of the particle of the TP samples were estimated to range from 0.70 µm to 3.01 µm for sintered and unsintered samples. In the LTP system, the highest conductivity obtained for the unsintered sample, LTP 15 and sintered LTP 15 (LTP 900) is 6.89 x 10-6 Scm-1 and 3.03 x 10-5 Scm-1 respectively. The diffraction pattern indicate the presence of LiTi2(P04)3 peaks which is the conducting phase.Small grains were observed in all sintered samples with increase in as sintering temperature increases. The sizes of particle of LTP samples were decreased to as low as 200 nm. Temperature dependance studied showed that the conductivity obeys Arrhenius rule indicating that the conductivity is thermally activated.
format	Thesis
author	Ahmad Faizal, Ahmad Fuzairi
author_facet	Ahmad Faizal, Ahmad Fuzairi
author_sort	Ahmad Faizal, Ahmad Fuzairi
title	Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal
title_short	Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal
title_full	Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal
title_fullStr	Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal
title_full_unstemmed	Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal
title_sort	mechanochemical synthesised solid electrolyte based on li2o : electrical and structural properties / ahmad fuzairi ahmad faizal
publishDate	2014
url	http://ir.uitm.edu.my/id/eprint/13820/ http://ir.uitm.edu.my/id/eprint/13820/1/TM_AHMAD%20FUZAIRI%20AHMAD%20FAIZAL%20AS%2014_5%201.pdf
first_indexed	2023-09-18T22:50:21Z
last_indexed	2023-09-18T22:50:21Z
_version_	1777417502722097152

Mechanochemical synthesised solid electrolyte based on Li2O : electrical and structural properties / Ahmad Fuzairi Ahmad Faizal

Similar Items