The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan

Centel/a asiatica nanopowders were produced using planetary ball mill. Parametric studies were done to determine the optimum parameters to produce smaller particles size (nanometer) and at the same time yield the highest extraction yield of asiatic acid. The milling parameters includes the effect o...

Full description

Bibliographic Details
Main Author:	Borhan, Muhammad Zuhairi
Format:	Thesis
Language:	English
Published:	2014
Subjects:	Antibacterial agents
Online Access:	http://ir.uitm.edu.my/id/eprint/14081/ http://ir.uitm.edu.my/id/eprint/14081/1/TM_MUHAMMAD%20ZUHAIRI%20BORHAN%20AS%2014_5.pdf

id	uitm-14081
recordtype	eprints
spelling	uitm-140812016-06-20T06:56:44Z http://ir.uitm.edu.my/id/eprint/14081/ The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan Borhan, Muhammad Zuhairi Antibacterial agents Centel/a asiatica nanopowders were produced using planetary ball mill. Parametric studies were done to determine the optimum parameters to produce smaller particles size (nanometer) and at the same time yield the highest extraction yield of asiatic acid. The milling parameters includes the effect of bead size (2 and 4 mm, in diameter), effect of mass concentration (0.4-2.8 w/v, %) effect of milling time (2-8 hours) and lastly effect of bead amount (5-100g). The size reduction was carried out in a wet mill with a fixed amount of solvent of 25 ml for each milling set and ultrapure water was used as a milling solvent. The Centella asiatica nanopowders were then analysed using several analytical techniques which are Spectroscopy (Pf.S), Field Emission scanning electron microscope (FESEM) and high performance liquid chromatography (HPLC).Based on the inspection of the Centella asiatica particles size and extraction yield of asiatic acid, it was found that the following parameters can be considered as the optimized parameter to produce higher quality of Cente/la asiatica nanopowders; the bead size and amount; 2mm and 25g, milling at 4 hours and produced at 1.2 (w/v,%) mass concentration where the size of particles ground at this condition is 283 nm in average and extraction yield of asiatic acid with 25mg/g. The morphology of nanopowders shows that the particles exist in agglomerated particles with size of grain below 1 urn, In this study, possible extraction mechanism is also establish to show difference from microparticles. The properties that contribute to the improved extraction yield of asiatic acid using nanopowders also were explained. The heavy metal analysis was also carried out on the nanopowders. The results were compared with micropowders because the heavy metal contamination is a seriously concern in herbal powder preparation. Results show nanopowders contain higher heavy metal content. However, the concentrations of heavy metals are still in the permissible range. Last but not least, this study also investigated the water extraction yield of asiatic acid between nanopowders and micropowders that shows the elevation of asiatic acid content in the water extract. In a nutshell, it can be concluded that the production of nanopowders can improve extraction yield of active compound and may revolutionize the sample preparation of herbal medicine in a future. 2014 Thesis NonPeerReviewed text en http://ir.uitm.edu.my/id/eprint/14081/1/TM_MUHAMMAD%20ZUHAIRI%20BORHAN%20AS%2014_5.pdf Borhan, Muhammad Zuhairi (2014) The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan. Masters thesis, Universiti Teknologi MARA.
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Teknologi MARA
building	UiTM Institutional Repository
collection	Online Access
language	English
topic	Antibacterial agents
spellingShingle	Antibacterial agents Borhan, Muhammad Zuhairi The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan
description	Centel/a asiatica nanopowders were produced using planetary ball mill. Parametric studies were done to determine the optimum parameters to produce smaller particles size (nanometer) and at the same time yield the highest extraction yield of asiatic acid. The milling parameters includes the effect of bead size (2 and 4 mm, in diameter), effect of mass concentration (0.4-2.8 w/v, %) effect of milling time (2-8 hours) and lastly effect of bead amount (5-100g). The size reduction was carried out in a wet mill with a fixed amount of solvent of 25 ml for each milling set and ultrapure water was used as a milling solvent. The Centella asiatica nanopowders were then analysed using several analytical techniques which are Spectroscopy (Pf.S), Field Emission scanning electron microscope (FESEM) and high performance liquid chromatography (HPLC).Based on the inspection of the Centella asiatica particles size and extraction yield of asiatic acid, it was found that the following parameters can be considered as the optimized parameter to produce higher quality of Cente/la asiatica nanopowders; the bead size and amount; 2mm and 25g, milling at 4 hours and produced at 1.2 (w/v,%) mass concentration where the size of particles ground at this condition is 283 nm in average and extraction yield of asiatic acid with 25mg/g. The morphology of nanopowders shows that the particles exist in agglomerated particles with size of grain below 1 urn, In this study, possible extraction mechanism is also establish to show difference from microparticles. The properties that contribute to the improved extraction yield of asiatic acid using nanopowders also were explained. The heavy metal analysis was also carried out on the nanopowders. The results were compared with micropowders because the heavy metal contamination is a seriously concern in herbal powder preparation. Results show nanopowders contain higher heavy metal content. However, the concentrations of heavy metals are still in the permissible range. Last but not least, this study also investigated the water extraction yield of asiatic acid between nanopowders and micropowders that shows the elevation of asiatic acid content in the water extract. In a nutshell, it can be concluded that the production of nanopowders can improve extraction yield of active compound and may revolutionize the sample preparation of herbal medicine in a future.
format	Thesis
author	Borhan, Muhammad Zuhairi
author_facet	Borhan, Muhammad Zuhairi
author_sort	Borhan, Muhammad Zuhairi
title	The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan
title_short	The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan
title_full	The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan
title_fullStr	The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan
title_full_unstemmed	The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan
title_sort	effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / muhammad zuhairi borhan
publishDate	2014
url	http://ir.uitm.edu.my/id/eprint/14081/ http://ir.uitm.edu.my/id/eprint/14081/1/TM_MUHAMMAD%20ZUHAIRI%20BORHAN%20AS%2014_5.pdf
first_indexed	2023-09-18T22:50:50Z
last_indexed	2023-09-18T22:50:50Z
_version_	1777417532258385920

The effect of milling parameters on extraction yield of asiaticoside and asiatic acid from centella asiatica nanopowders / Muhammad Zuhairi Borhan

Similar Items