Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]

The pyrolysis of Meranti wood was investigated in a static batch reactor at low pyrolysis temperatures 300°C,350°C and 400 °C. The compositions and properties of the derived gases, pyrolytic oils and solid char were determined with respect to pyrolysis temperature. Preliminary experiment was conduct...

Full description

Bibliographic Details
Format:	Article
Language:	English
Published:	Faculty of Mechanical Engineering and University Publication Centre (UPENA) 2008
Online Access:	http://ir.uitm.edu.my/id/eprint/17571/ http://ir.uitm.edu.my/id/eprint/17571/1/AJ_NORAISHAH%20OTHMAN%20JME%2008.pdf

id	uitm-17571
recordtype	eprints
spelling	uitm-175712017-08-01T04:07:15Z http://ir.uitm.edu.my/id/eprint/17571/ Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.] The pyrolysis of Meranti wood was investigated in a static batch reactor at low pyrolysis temperatures 300°C,350°C and 400 °C. The compositions and properties of the derived gases, pyrolytic oils and solid char were determined with respect to pyrolysis temperature. Preliminary experiment was conducted using thermogravimetric analyzer (TGA) to determine the active range of temperature occurrence during thermal decompositions on the Meranti wood. Different heating rates (20°C/min, 30°C/min and 40°C/min) were applied to look at the effect of heating rate on the wood. The static batch reactor showed that at low temperature, the percentage of char was higher compared to char production at high temperature. Nevertheless, the oil product at low temperature was lower compared to at high temperature and gas production was slightly similar for both conditions. There was a small effect of heating rates on the active pyrolysis rate. All heating rates showed the range of300°C to 400 °C as the active pyrolysis rate. Faculty of Mechanical Engineering and University Publication Centre (UPENA) 2008 Article PeerReviewed text en http://ir.uitm.edu.my/id/eprint/17571/1/AJ_NORAISHAH%20OTHMAN%20JME%2008.pdf UNSPECIFIED (2008) Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]. Journal of Mechanical Engineering, 5 (2). pp. 73-80. ISSN 1823-5514
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Teknologi MARA
building	UiTM Institutional Repository
collection	Online Access
language	English
description	The pyrolysis of Meranti wood was investigated in a static batch reactor at low pyrolysis temperatures 300°C,350°C and 400 °C. The compositions and properties of the derived gases, pyrolytic oils and solid char were determined with respect to pyrolysis temperature. Preliminary experiment was conducted using thermogravimetric analyzer (TGA) to determine the active range of temperature occurrence during thermal decompositions on the Meranti wood. Different heating rates (20°C/min, 30°C/min and 40°C/min) were applied to look at the effect of heating rate on the wood. The static batch reactor showed that at low temperature, the percentage of char was higher compared to char production at high temperature. Nevertheless, the oil product at low temperature was lower compared to at high temperature and gas production was slightly similar for both conditions. There was a small effect of heating rates on the active pyrolysis rate. All heating rates showed the range of300°C to 400 °C as the active pyrolysis rate.
format	Article
title	Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]
spellingShingle	Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]
title_short	Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]
title_full	Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]
title_fullStr	Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]
title_full_unstemmed	Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]
title_sort	study of product yields from degraded meranti woods for the low temperature pyrolysis process using static batch reactor / noraishah othman … [et al.]
publisher	Faculty of Mechanical Engineering and University Publication Centre (UPENA)
publishDate	2008
url	http://ir.uitm.edu.my/id/eprint/17571/ http://ir.uitm.edu.my/id/eprint/17571/1/AJ_NORAISHAH%20OTHMAN%20JME%2008.pdf
first_indexed	2023-09-18T22:58:35Z
last_indexed	2023-09-18T22:58:35Z
_version_	1777418020741709824

Study of product yields from degraded Meranti Woods for the low temperature pyrolysis process using static batch reactor / Noraishah Othman … [et al.]

Similar Items