Performance of finger joint from Sepetir / Yuhanis Yunus
This study was conducted to evaluate the effects of pressure on performance of the finger joint. The wood species studied were sepetir (sindofa spp) and adhesives were poly (vinyl acetate) (PVAc).However, there is little information available concerning the bending strength and modulus of elastic...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty Of Applied Sciences
2015
|
| Subjects: | |
| Online Access: | http://ir.uitm.edu.my/id/eprint/22837/ http://ir.uitm.edu.my/id/eprint/22837/1/PPb_YUHANIS%20YUNUS%20AS%20C%2015_5.PDF |
| Summary: | This study was conducted to evaluate the effects of pressure on performance
of the finger joint. The wood species studied were sepetir (sindofa spp) and
adhesives were poly (vinyl acetate) (PVAc).However, there is little information
available concerning the bending strength and modulus of elasticity and
modulus of rupture for finger joints in these field. In this study, it was aimed to
determine the bending strength and modulus of elasticity and modulus of
rupture for finger joints. For this purpose, samples were tested according to
the ASTM 05572 - 95(2012) standard. The pressure apply on the finger joint
is different, 1MPa 2MPa 3MPa. Result of the study 1MPa shown that it is the
best pressure can be applied on the joint. It can be concluded that the result
of pressure on sepetir wood is match to previous study and suitable to be
commercialized. |
|---|