Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki

Metal Injection Moulding (MIM) process is an economically attractive method of producing large amounts of small and complex metallic parts. This is achieved by combining the productivity of injection moulding with the versatility of sintering metal particulates. In MIM, the powdered metal is blen...

Full description

Bibliographic Details
Main Author:	Subuki, Istikamah
Format:	Thesis
Language:	English
Published:	2010
Subjects:	Stainless steel TJ Mechanical engineering and machinery
Online Access:	http://ir.uitm.edu.my/id/eprint/4266/ http://ir.uitm.edu.my/id/eprint/4266/1/TP_ISTIKAMAH%20SUBUKI%20EM%2010_5%201.pdf

id	uitm-4266
recordtype	eprints
spelling	uitm-42662016-11-21T15:08:23Z http://ir.uitm.edu.my/id/eprint/4266/ Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki Subuki, Istikamah Stainless steel TJ Mechanical engineering and machinery Metal Injection Moulding (MIM) process is an economically attractive method of producing large amounts of small and complex metallic parts. This is achieved by combining the productivity of injection moulding with the versatility of sintering metal particulates. In MIM, the powdered metal is blended with a binder to obtain a feedstock. The binder imparts flowability to the blend at injection moulding conditions and strength at ambient conditions. After moulding, the binder is removed in a sequence of steps that usually involves solvent extraction and thermal pyrolysis. Once the binder is removed, the metal particles are sintered. Accordingly, though the binder should not dictate the final composition, it has an influence on the process. Today, new local binder composition and its effectiveness as a binder system to all type of metal powder are the focus of many investigations. In this research work, a gas atomised 316L stainless steel (SS) powder with different particle size (16 μm and 45 μm) were evaluated using a locally binder system comprising a major fraction of palm stearin (PS) and polyethylene (PE). All the feedstock prepared shows homogeneity with pseudoplastic behaviour which is suitable for MIM process. Feedstock was prepared in a Z-blade mixer for batch mixing and subsequent injection moulding was carried out to form a tensile specimen. Prior to sintering, the moulded specimen were leached in heptane to remove the PS and then heated in furnace to remove the remaining PE binder. Some defect was detected for the specimen made with courser powder after being thermal pyrolysis. However, for fine powder (16 μm), all specimens were in good condition. After being sintered, the specimen gives 91% of the theoretical density. In order to achieve high density of sintered specimen, the powder loading was increase to the optimum powder loading of 65 vol.% and these results in specimens with 97.6% theoretical density. The influence of PS content was optimised in order to make full use of this in MIM work. Experimental evidence showed that the maximum content of PS in binder system allowable is up to 70 wt.%. The result also showed that increasing the PS content may shorten the overall debinding process and higher sintered density of 99.1% of theoretical maximum value can be achieved. Besides PS/PE system, another backbone binder; polypropylene (PP) with different composition was evaluated to show the interaction with PS. Although the rheological properties show dilatant behaviour, the feedstock was successfully injection moulded and achieved high density of green specimen. Moreover, the specimen was easy to handle during solvent extraction and thermal pyrolysis. Higher sintered density of 99.25% was achieved as compared to PS/PE binder formulation. Introduction of stearic acid (SA) in the binder that act as a lubricant helped in the mixing process to produce a homogeneous blend and the torque reached a steady state value in a short time. Increasing the stearic acid in the binder system resulted in lowered viscosity, thus improving the injection mouldability of the feedstock. This new developed binder, PS can also be injection moulded with water atomised 316L stainless steel powder, and the density achieved is 96% that of theoretical density. High physical and mechanical properties of the sintered specimen can be achieved as sintered at the temperature of 1360 oC with the heating rate of 10 oC/min under vacuum atmosphere followed by 95% N2/5% H2 and argon condition. 2010 Thesis NonPeerReviewed text en http://ir.uitm.edu.my/id/eprint/4266/1/TP_ISTIKAMAH%20SUBUKI%20EM%2010_5%201.pdf Subuki, Istikamah (2010) Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki. PhD thesis, Universiti Teknologi MARA.
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Teknologi MARA
building	UiTM Institutional Repository
collection	Online Access
language	English
topic	Stainless steel TJ Mechanical engineering and machinery
spellingShingle	Stainless steel TJ Mechanical engineering and machinery Subuki, Istikamah Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki
description	Metal Injection Moulding (MIM) process is an economically attractive method of producing large amounts of small and complex metallic parts. This is achieved by combining the productivity of injection moulding with the versatility of sintering metal particulates. In MIM, the powdered metal is blended with a binder to obtain a feedstock. The binder imparts flowability to the blend at injection moulding conditions and strength at ambient conditions. After moulding, the binder is removed in a sequence of steps that usually involves solvent extraction and thermal pyrolysis. Once the binder is removed, the metal particles are sintered. Accordingly, though the binder should not dictate the final composition, it has an influence on the process. Today, new local binder composition and its effectiveness as a binder system to all type of metal powder are the focus of many investigations. In this research work, a gas atomised 316L stainless steel (SS) powder with different particle size (16 μm and 45 μm) were evaluated using a locally binder system comprising a major fraction of palm stearin (PS) and polyethylene (PE). All the feedstock prepared shows homogeneity with pseudoplastic behaviour which is suitable for MIM process. Feedstock was prepared in a Z-blade mixer for batch mixing and subsequent injection moulding was carried out to form a tensile specimen. Prior to sintering, the moulded specimen were leached in heptane to remove the PS and then heated in furnace to remove the remaining PE binder. Some defect was detected for the specimen made with courser powder after being thermal pyrolysis. However, for fine powder (16 μm), all specimens were in good condition. After being sintered, the specimen gives 91% of the theoretical density. In order to achieve high density of sintered specimen, the powder loading was increase to the optimum powder loading of 65 vol.% and these results in specimens with 97.6% theoretical density. The influence of PS content was optimised in order to make full use of this in MIM work. Experimental evidence showed that the maximum content of PS in binder system allowable is up to 70 wt.%. The result also showed that increasing the PS content may shorten the overall debinding process and higher sintered density of 99.1% of theoretical maximum value can be achieved. Besides PS/PE system, another backbone binder; polypropylene (PP) with different composition was evaluated to show the interaction with PS. Although the rheological properties show dilatant behaviour, the feedstock was successfully injection moulded and achieved high density of green specimen. Moreover, the specimen was easy to handle during solvent extraction and thermal pyrolysis. Higher sintered density of 99.25% was achieved as compared to PS/PE binder formulation. Introduction of stearic acid (SA) in the binder that act as a lubricant helped in the mixing process to produce a homogeneous blend and the torque reached a steady state value in a short time. Increasing the stearic acid in the binder system resulted in lowered viscosity, thus improving the injection mouldability of the feedstock. This new developed binder, PS can also be injection moulded with water atomised 316L stainless steel powder, and the density achieved is 96% that of theoretical density. High physical and mechanical properties of the sintered specimen can be achieved as sintered at the temperature of 1360 oC with the heating rate of 10 oC/min under vacuum atmosphere followed by 95% N2/5% H2 and argon condition.
format	Thesis
author	Subuki, Istikamah
author_facet	Subuki, Istikamah
author_sort	Subuki, Istikamah
title	Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki
title_short	Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki
title_full	Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki
title_fullStr	Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki
title_full_unstemmed	Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki
title_sort	injection moulding of 316l stainless steel powder using palm stearin based binder system / istikamah subuki
publishDate	2010
url	http://ir.uitm.edu.my/id/eprint/4266/ http://ir.uitm.edu.my/id/eprint/4266/1/TP_ISTIKAMAH%20SUBUKI%20EM%2010_5%201.pdf
first_indexed	2023-09-18T22:46:54Z
last_indexed	2023-09-18T22:46:54Z
_version_	1777417285758091264

Injection moulding of 316L stainless steel powder using palm stearin based binder system / Istikamah Subuki

Similar Items