Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method

The aim of this study was to investigate the effect of structural orientation on the impedance and piezoelectric properties of Ka0.5Na0.5NbO3 (KNN) ceramic synthesized using modified sol-gel method. Dried xerogel was heated at 800oC for 90 min and the aggregates were grinded to powder form. SEM micr...

Full description

Bibliographic Details
Main Authors:	I. Izzuddin, M.H.H. Jumali, Z. Zalita, J.N. Huwaida, R. Awang
Format:	Article
Language:	English
Published:	Penerbit Universiti Kebangsaan Malaysia 2016
Online Access:	http://journalarticle.ukm.my/10188/ http://journalarticle.ukm.my/10188/ http://journalarticle.ukm.my/10188/1/15%20I.%20Izzuddin.pdf

id	ukm-10188
recordtype	eprints
spelling	ukm-101882017-03-03T09:04:49Z http://journalarticle.ukm.my/10188/ Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method I. Izzuddin, M.H.H. Jumali, Z. Zalita, J.N. Huwaida, R. Awang, The aim of this study was to investigate the effect of structural orientation on the impedance and piezoelectric properties of Ka0.5Na0.5NbO3 (KNN) ceramic synthesized using modified sol-gel method. Dried xerogel was heated at 800oC for 90 min and the aggregates were grinded to powder form. SEM micrographs confirmed that the powder consist of bimodal particles in nm and μm size regimes. The powder was compacted into 13 mm diameter pellet and sintered at 1000oC for 6 h. Then the pellets were poled at 4.0kV/mm at 100oC for 30 min. The as-sintered pellets displayed different sizes of cuboidal granules forming a relatively dense sample. The XRD and Raman spectroscopy results confirmed the formation of perovskite KNN with monoclinic crystal structure. The compositional analysis using Vegard’s law showed that the K:Na ratio was 0.5:0.5. Dramatic intensity enhancement in (110) reflection and subsequent reduction in (100) reflection as observed in X-ray diffractograms for the poled pellet suggest permanent shift in crystal orientation. Consequently, the Nyquist impedance plot of a Debye type semicircular arc was altered to a combination of a depressed semicircular arc. Unlike the initial plot, the real impedance, Z′ exhibited frequency dependence at low frequency regime. In addition, the relaxation time, τ of KNN sample shifted to lower frequency after the structural re-orientation while piezoelectric constant, d33 along (110) direction significantly improved from 5 to 35 pC/N. Penerbit Universiti Kebangsaan Malaysia 2016-08 Article PeerReviewed application/pdf en http://journalarticle.ukm.my/10188/1/15%20I.%20Izzuddin.pdf I. Izzuddin, and M.H.H. Jumali, and Z. Zalita, and J.N. Huwaida, and R. Awang, (2016) Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method. Sains Malaysiana, 45 (8). pp. 1281-1287. ISSN 0126-6039 http://www.ukm.my/jsm/english_journals/vol45num8_2016/contentsVol45num8_2016.html
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Kebangasaan Malaysia
building	UKM Institutional Repository
collection	Online Access
language	English
description	The aim of this study was to investigate the effect of structural orientation on the impedance and piezoelectric properties of Ka0.5Na0.5NbO3 (KNN) ceramic synthesized using modified sol-gel method. Dried xerogel was heated at 800oC for 90 min and the aggregates were grinded to powder form. SEM micrographs confirmed that the powder consist of bimodal particles in nm and μm size regimes. The powder was compacted into 13 mm diameter pellet and sintered at 1000oC for 6 h. Then the pellets were poled at 4.0kV/mm at 100oC for 30 min. The as-sintered pellets displayed different sizes of cuboidal granules forming a relatively dense sample. The XRD and Raman spectroscopy results confirmed the formation of perovskite KNN with monoclinic crystal structure. The compositional analysis using Vegard’s law showed that the K:Na ratio was 0.5:0.5. Dramatic intensity enhancement in (110) reflection and subsequent reduction in (100) reflection as observed in X-ray diffractograms for the poled pellet suggest permanent shift in crystal orientation. Consequently, the Nyquist impedance plot of a Debye type semicircular arc was altered to a combination of a depressed semicircular arc. Unlike the initial plot, the real impedance, Z′ exhibited frequency dependence at low frequency regime. In addition, the relaxation time, τ of KNN sample shifted to lower frequency after the structural re-orientation while piezoelectric constant, d33 along (110) direction significantly improved from 5 to 35 pC/N.
format	Article
author	I. Izzuddin, M.H.H. Jumali, Z. Zalita, J.N. Huwaida, R. Awang,
spellingShingle	I. Izzuddin, M.H.H. Jumali, Z. Zalita, J.N. Huwaida, R. Awang, Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method
author_facet	I. Izzuddin, M.H.H. Jumali, Z. Zalita, J.N. Huwaida, R. Awang,
author_sort	I. Izzuddin,
title	Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method
title_short	Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method
title_full	Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method
title_fullStr	Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method
title_full_unstemmed	Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method
title_sort	influence of crystal structural orientation on impedance and piezoelectric properties of knn ceramic prepared using sol-gel method
publisher	Penerbit Universiti Kebangsaan Malaysia
publishDate	2016
url	http://journalarticle.ukm.my/10188/ http://journalarticle.ukm.my/10188/ http://journalarticle.ukm.my/10188/1/15%20I.%20Izzuddin.pdf
first_indexed	2023-09-18T19:56:45Z
last_indexed	2023-09-18T19:56:45Z
_version_	1777406580278427648

Influence of crystal structural orientation on impedance and piezoelectric properties of KNN ceramic prepared using sol-gel method

Similar Items