Subsolidus solution and oxide ionic conductivity of Nd-substituted Bismuth Yttria Fluorites
Pure phase Bi1.6Y0.4-xNdxO3 solid solution with x = 0.00, 0.10 and 0.20 was successfully synthesised via conventional solid state method at 850°C in 21 h. The materials were refined and fully indexed with space group Fm-3m and lattice parameters, a ranging from 5.5124(1) Å to 5.5289(4) Å. Variation...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universiti Kebangsaan Malaysia
2015
|
| Online Access: | http://journalarticle.ukm.my/8986/ http://journalarticle.ukm.my/8986/ http://journalarticle.ukm.my/8986/1/12_K.B._Tan.pdf |
| Summary: | Pure phase Bi1.6Y0.4-xNdxO3 solid solution with x = 0.00, 0.10 and 0.20 was successfully synthesised via conventional solid state method at 850°C in 21 h. The materials were refined and fully indexed with space group Fm-3m and lattice parameters, a ranging from 5.5124(1) Å to 5.5289(4) Å. Variation of the lattice parameters of these materials were found in an almost linear correlation with increasing Nd2O3 dopant concentration. Thermal analysis of Bi1.6Y0.4-xNdxO3 solid solution showed no thermal event that associated with any phase transition or weight loss within the studied temperature range of 35 to 900°C. The electrical properties of the samples were investigated by ac impedance analyser, HP4192 at temperature ranging from 25 to 800°C over frequency of 5 Hz to 13 MHz. Bi1.6Y0.3Nd0.1O3 exhibited the highest oxide ion conductivity among the synthesised samples in Bi1.6Y0.4-xNdxO3 solid solution. |
|---|