Photo-polishing of POME into CH4-Lean Biogas over The UV-Responsive ZnO Photocatalyst
We report here the photo-polishing of POME with a concomitant production of CH4-lean biogas over UV/ZnO photocatalysis system. The photoreaction results showed that the optimum ZnO loading for POME photomineralization was 1.0 g/L, with about 50% of COD removal after just 240 min of UV irradiation...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
Elsevier
2016
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/12990/ http://umpir.ump.edu.my/id/eprint/12990/ http://umpir.ump.edu.my/id/eprint/12990/1/UMP-IR-Chem-Eng%20J.pdf http://umpir.ump.edu.my/id/eprint/12990/7/Photo-polishing%20of%20POME%20into%20CH4-lean%20biogas%20over%20the%20UV-responsive%20ZnO%20photocatalyst.pdf |
| Summary: | We report here the photo-polishing of POME with a concomitant production of CH4-lean biogas over UV/ZnO photocatalysis system. The photoreaction results showed that the optimum ZnO loading for POME photomineralization was 1.0 g/L, with about 50% of COD removal after just
240 min of UV irradiation. It is found that all the photomineralization kinetics can be modelled to the 1st-order reaction order, with specific reaction rates (k)ranging from 1.022 × 10-3 to 3.118 × 10-3 min-1. The highest amount of gaseous products, viz. 36,172 µmol of CO2and 333 µmol of CH4, were produced at this optimum loading. Significantly, the organic removal efficiency was
further enhanced when the UV exposure was prolonged to 22 h, attaining final readings of 44 ppm, 26 ppm and 20 mg/L, respectively, for chemical oxygen demand (COD), biochemical
oxygen demand (BOD) and oil and grease (O&G). Furthermore, our scavenging study suggests that the photomineralization of organic pollutants in the POME occurred via attack by the highly reactive OH• radical. In addition, we posit that the reaction took place on the surface of ZnO2 upon the adsorption of the organic pollutants. Our proposition was further confirmed by the presence of carbonaceous species on the surface of ZnO through a combination of spectroscopic
probes, i.e. FTIR, SEM-EDX, as well as the deterioration in the BET specific surface area for the used ZnO photocatalyst. The plunge of ZnO’s photodegradation performance was observed in the recyclability test. The performance has plummeted from 50% to 35% in second cycle before stabilizing at 38% in the third cycle. This can be attributed to the blockage of surface area of ZnO by the deposited organic species. |
|---|