Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy

The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix...

Full description

Bibliographic Details
Main Authors:	Iqbal, AKM Asif, Arai, Yoshio
Format:	Conference or Workshop Item
Language:	English English
Published:	2016
Subjects:	TS Manufactures
Online Access:	http://umpir.ump.edu.my/id/eprint/14055/ http://umpir.ump.edu.my/id/eprint/14055/1/Stress%20Measurement%20During%20Crack%20Propagation%20In%20Metal%20Matrix%20Composites%20Using%20Micro-Raman%20Spectroscopy.pdf http://umpir.ump.edu.my/id/eprint/14055/7/fkp-2016-asif-Stress%20Measurement%20During%20Crack%20Propagation.pdf

id	ump-14055
recordtype	eprints
spelling	ump-140552018-02-23T03:35:31Z http://umpir.ump.edu.my/id/eprint/14055/ Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy Iqbal, AKM Asif Arai, Yoshio TS Manufactures The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix interface and particle fracture. A high decrease in stress was observed with the interfacial debonding at the interface and with the particle fracture on the particle. Moreover, the critical tensile stresses for particle-matrix interface debonding and particle fracture developed in hybrid MMC were also estimated during the crack propagation. 2016 Conference or Workshop Item NonPeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/14055/1/Stress%20Measurement%20During%20Crack%20Propagation%20In%20Metal%20Matrix%20Composites%20Using%20Micro-Raman%20Spectroscopy.pdf application/pdf en http://umpir.ump.edu.my/id/eprint/14055/7/fkp-2016-asif-Stress%20Measurement%20During%20Crack%20Propagation.pdf Iqbal, AKM Asif and Arai, Yoshio (2016) Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy. In: 17th European Conference on Composite Materials (ECCM17), 26-30 June 2016 , Munich, Germany. pp. 1-8.. (Unpublished)
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Malaysia Pahang
building	UMP Institutional Repository
collection	Online Access
language	English English
topic	TS Manufactures
spellingShingle	TS Manufactures Iqbal, AKM Asif Arai, Yoshio Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
description	The measurement of stress in the SiC particles during crack propagation was investigated by micro raman spectroscopy. The experiment was carried out in situ in the Raman spectroscopy. Experimental results showed that cracks due to monotonic loading propagated by the debonding of the particle/matrix interface and particle fracture. A high decrease in stress was observed with the interfacial debonding at the interface and with the particle fracture on the particle. Moreover, the critical tensile stresses for particle-matrix interface debonding and particle fracture developed in hybrid MMC were also estimated during the crack propagation.
format	Conference or Workshop Item
author	Iqbal, AKM Asif Arai, Yoshio
author_facet	Iqbal, AKM Asif Arai, Yoshio
author_sort	Iqbal, AKM Asif
title	Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
title_short	Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
title_full	Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
title_fullStr	Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
title_full_unstemmed	Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy
title_sort	stress measurement during crack propagation in metal matrix composites using micro-raman spectroscopy
publishDate	2016
url	http://umpir.ump.edu.my/id/eprint/14055/ http://umpir.ump.edu.my/id/eprint/14055/1/Stress%20Measurement%20During%20Crack%20Propagation%20In%20Metal%20Matrix%20Composites%20Using%20Micro-Raman%20Spectroscopy.pdf http://umpir.ump.edu.my/id/eprint/14055/7/fkp-2016-asif-Stress%20Measurement%20During%20Crack%20Propagation.pdf
first_indexed	2023-09-18T22:17:22Z
last_indexed	2023-09-18T22:17:22Z
_version_	1777415427459121152

Stress Measurement During Crack Propagation In Metal Matrix Composites Using Micro-Raman Spectroscopy

Similar Items