Effect of degassing addition on the solidification of nickel aluminum bronze
The effect of degassing agent addition on the solidification of Nickel Aluminum Bronze was investigated. The complex relationship between the development of the alloy solidification and its thermal analysis in Nickel Aluminum Bronze was obtained by using data logger. This experiment describes the ch...
Main Authors: | , , , , |
---|---|
Format: | Conference or Workshop Item |
Language: | English English |
Published: |
AIP Publishing LLC
2018
|
Subjects: | |
Online Access: | http://umpir.ump.edu.my/id/eprint/24352/ http://umpir.ump.edu.my/id/eprint/24352/ http://umpir.ump.edu.my/id/eprint/24352/1/76.%20Effect%20of%20degassing%20addition%20on%20the%20solidification.pdf http://umpir.ump.edu.my/id/eprint/24352/2/76.1%20Effect%20of%20degassing%20addition%20on%20the%20solidification.pdf |
Summary: | The effect of degassing agent addition on the solidification of Nickel Aluminum Bronze was investigated. The complex relationship between the development of the alloy solidification and its thermal analysis in Nickel Aluminum Bronze was obtained by using data logger. This experiment describes the characterization of thermal analysis in Nickel Aluminum Bronze which was interpret using solidification cooling curve. With this method, the differences of temperature points during solidification were clearly evidenced. The results show a solidification cooling curve directly affected by percentage of degassing agent added in molten Nickel Aluminum Bronze alloy. There is distribution of temperature point after solidification from melting. As for degassing treatment, higher degassing addition on the Nickel Aluminum Bronze decreased the solidification temperature point. |
---|