Electrical Properties of A Novel Solid Biopolymer Electrolyte based on Algi-nate Incorporated with Citric Acid
In the present study, a novel solid biopolymer electrolytes (SBE) system has been introduced by doping citric acid into alginate polymer. The sample of alginate-citric acid SBE system was prepared via solution casting technique. By using Electrical Impedance Spectroscopy (EIS), the electrolytes of a...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
DRPM Universitas Indonesia
2019
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/24900/ http://umpir.ump.edu.my/id/eprint/24900/ http://umpir.ump.edu.my/id/eprint/24900/ http://umpir.ump.edu.my/id/eprint/24900/1/Electrical%20Properties%20of%20A%20Novel%20Solid%20Biopolymer%20Electrolyte1.pdf |
| Summary: | In the present study, a novel solid biopolymer electrolytes (SBE) system has been introduced by doping citric acid into alginate polymer. The sample of alginate-citric acid SBE system was prepared via solution casting technique. By using Electrical Impedance Spectroscopy (EIS), the electrolytes of alginate-citric acid has been analyzed from 5 Hz to 1 MHz achieved highest conductivity value at 20 wt.% of 5.49 x 10-7 S cm-1. The temperature dependence of various composition citric acid was found to obey the Arrhenius rules with R2~1 where all SBE system is thermally activated when increasing temperature. The dielectric studies of the alginate-citric acid SBE system showed a non-debye behavior based on data measured using complex permittivity (ε*) and complex electrical modulus (M*) at selected temperature where there are no single relation was found in new biopolymer electrolytes system. |
|---|