Microstructure and Mechanical Properties of Modified Ductile Ni-resist With Higher Manganese Content
In this study, ductile Ni-resist with a minimum of 18 wt % nickel composition was modified. Up to 12 wt % manganese was added together with 10 wt % nickel to investigate the effects of the alloying elements on both its microstructure and mechanical properties. Compared to un-modified ductile Ni-resi...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2013
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/3687/ http://umpir.ump.edu.my/id/eprint/3687/ http://umpir.ump.edu.my/id/eprint/3687/ http://umpir.ump.edu.my/id/eprint/3687/1/rashidi_and_hasbullah2.pdf |
| Summary: | In this study, ductile Ni-resist with a minimum of 18 wt % nickel composition was modified. Up to 12 wt % manganese was added together with 10 wt % nickel to investigate the effects of the alloying elements on both its microstructure and mechanical properties. Compared to un-modified ductile Ni-resist, the results show a higher manganese composition on modifying ductile Ni-resist that increases carbide formation and hardness, and decreases tensile strength. However, the composition obtained was an austenitic iron matrix with a mixed result of graphite – shape nodularity. It appears that manganese plays a significant role in stabilizing the austenitic matrix phase as well as encouraging carbide formation. |
|---|