Investigate the effectiveness of stop drill hole in delaying crack from crack initiation
Many failures in engineering applications or machine components have been caused by a crack initiated from points at which stress was concentrated. As the stress concentration level is higher than a critical value, continuous crack-growth results in failure in the machine components. Crack initiatio...
Main Author: | Syafiq, Hashim |
---|---|
Format: | Undergraduates Project Papers |
Language: | English |
Published: |
2012
|
Subjects: | |
Online Access: | http://umpir.ump.edu.my/id/eprint/4907/ http://umpir.ump.edu.my/id/eprint/4907/ http://umpir.ump.edu.my/id/eprint/4907/1/cd7282_113.pdf |
Similar Items
-
Investigation the delay of crack using stop drilled holes on mild steel
by: Ridzuan Shah Razi, Varathau Rajoo
Published: (2009) -
Parametric study on fatique failure using crack initiation method
by: Mohd Fadzrul Hisyam, Badarudin
Published: (2012) -
Investigation of chloride stress corrosion cracking in austenitic stainless steel
by: Mohamad Khairuazlan, Kamaruzaman
Published: (2013) -
Finite element based fatigue crack growth of cracked plates under axial loading
by: Mohamad Abiddullah, Mohd Lasim
Published: (2010) -
Investigation and monitoring of groundwater level: building crack near to IIUM Kuantan
by: Koay, B. K., et al.
Published: (2018)