Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel

One of the ways to prevent the corrosion from occurs is coating or painting. Paint is used as protector to the materials such as mild steel that prevent the corrosion to occur. Besides that, the corrosion rate in different concentration of Sodium Chloride (NaCl) solution is different. This study is...

Full description

Bibliographic Details
Main Author:	Mohd Firdaus, Ibrahim
Format:	Undergraduates Project Papers
Language:	English
Published:	2013
Subjects:	TA Engineering (General). Civil engineering (General)
Online Access:	http://umpir.ump.edu.my/id/eprint/8622/ http://umpir.ump.edu.my/id/eprint/8622/ http://umpir.ump.edu.my/id/eprint/8622/1/CD8025_%40_40.pdf

id	ump-8622
recordtype	eprints
spelling	ump-86222015-11-03T00:02:15Z http://umpir.ump.edu.my/id/eprint/8622/ Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel Mohd Firdaus, Ibrahim TA Engineering (General). Civil engineering (General) One of the ways to prevent the corrosion from occurs is coating or painting. Paint is used as protector to the materials such as mild steel that prevent the corrosion to occur. Besides that, the corrosion rate in different concentration of Sodium Chloride (NaCl) solution is different. This study is carried on the 5 sample of mild steel as specimen that immersed in different concentration of NaCl that is 0% of NaCl, 1.5% of NaCl, 2.5% of NaCl, 3.5% of NaCl and 4.5% of NaCl. This study is carried 6 days and the result is obtained by photo snapping at second day (2nd day), fourth day (4th day) and sixth day (6th day) continuously. The paint quality is analyzing from width of corrosion, peeling, wear off and changes in colour. After that, to obtain the corrosion rate, the mass loss experiment was carried out. The purpose of this study is to study the corrosion on coated steel in different concentration of NaCl solutions. Besides that, this study also to investigate the performance of protective coating on steel in different concentration of NaCl solutions. At the end of the experiment, we can conclude that the corrosion rate is increase when the concentration of NaCl solution is also increase. Other than that, the performance of the protective coating especially paint on steel is different when it immersed in the different concentration of NaCl that is the quality of paint in 4.5% of NaCl solution is most fast to decrease. 2013-06 Undergraduates Project Papers NonPeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/8622/1/CD8025_%40_40.pdf Mohd Firdaus, Ibrahim (2013) Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel. Faculty of Mechanical Engineering , Universiti Malaysia Pahang. http://iportal.ump.edu.my/lib/item?id=chamo:83868&theme=UMP2
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Malaysia Pahang
building	UMP Institutional Repository
collection	Online Access
language	English
topic	TA Engineering (General). Civil engineering (General)
spellingShingle	TA Engineering (General). Civil engineering (General) Mohd Firdaus, Ibrahim Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel
description	One of the ways to prevent the corrosion from occurs is coating or painting. Paint is used as protector to the materials such as mild steel that prevent the corrosion to occur. Besides that, the corrosion rate in different concentration of Sodium Chloride (NaCl) solution is different. This study is carried on the 5 sample of mild steel as specimen that immersed in different concentration of NaCl that is 0% of NaCl, 1.5% of NaCl, 2.5% of NaCl, 3.5% of NaCl and 4.5% of NaCl. This study is carried 6 days and the result is obtained by photo snapping at second day (2nd day), fourth day (4th day) and sixth day (6th day) continuously. The paint quality is analyzing from width of corrosion, peeling, wear off and changes in colour. After that, to obtain the corrosion rate, the mass loss experiment was carried out. The purpose of this study is to study the corrosion on coated steel in different concentration of NaCl solutions. Besides that, this study also to investigate the performance of protective coating on steel in different concentration of NaCl solutions. At the end of the experiment, we can conclude that the corrosion rate is increase when the concentration of NaCl solution is also increase. Other than that, the performance of the protective coating especially paint on steel is different when it immersed in the different concentration of NaCl that is the quality of paint in 4.5% of NaCl solution is most fast to decrease.
format	Undergraduates Project Papers
author	Mohd Firdaus, Ibrahim
author_facet	Mohd Firdaus, Ibrahim
author_sort	Mohd Firdaus, Ibrahim
title	Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel
title_short	Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel
title_full	Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel
title_fullStr	Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel
title_full_unstemmed	Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel
title_sort	effect of different sodium chloride (nacl) concentration on corrosion of coated steel
publishDate	2013
url	http://umpir.ump.edu.my/id/eprint/8622/ http://umpir.ump.edu.my/id/eprint/8622/ http://umpir.ump.edu.my/id/eprint/8622/1/CD8025_%40_40.pdf
first_indexed	2023-09-18T22:06:23Z
last_indexed	2023-09-18T22:06:23Z
_version_	1777414736691855360

Effect of different sodium chloride (NaCl) concentration on corrosion of coated steel

Similar Items