Pack cementation of high chromium steel for high temperature application in steam condition
The oxidation of high Chromium (Cr) steels in steam environment may cause retardation or evaporation of protective chromia (Cr2O3) layer, which reduces its corrosion resistance as boiler materials. This condition may cause reduction of boiler life time or failure during operation. Therefore, the eff...